A簡介
Romania STAS/SR Structure Steel A，及該型號鋼材的基本信息、化學元素成分、機械性能、力學性能、熱處理溫度、同等型號參照表等。
基本信息：
| 分類 |
種類 |
型號 |
標準 |
國家 |
應(yīng)用 |
|---|
| Steel Grades |
|
A |
STAS/SR |
Romania |
Structural steel |
化學成分信息(mass fraction)(wt.%) of the A：
| 元素名稱 |
含量比例值 |
|---|
| C |
0.23 |
| Si |
Min 0.35 |
| Mn |
Min 2.5xC |
| P |
0.050 |
| S |
0.050 |
| Cr |
0.30 |
| Ni |
Max 0.30 |
機械性能信息：
| 屈服強度Rp0.2（MPa） |
抗拉強度Rm（MPa） |
沖擊率 |
伸長率 |
斷面收縮率 |
熱處理狀態(tài) |
布氏硬度（HBW） |
|---|
| 848 (≥) |
535 (≥) |
23 |
43 |
23 |
Solution and Aging, Annealing, Ausaging, Q+T,etc |
433 |
物理性質(zhì)信息：
| 溫度 |
彈性模量 |
系數(shù) |
熱導(dǎo)率 |
比熱容量 |
比電阻率 |
密度 |
加權(quán)系數(shù) |
|---|
| 21 |
- |
- |
|
|
0.14 |
- |
|
| 728 |
955 |
- |
43.3 |
441 |
|
- |
|
| 532 |
- |
42 |
33.2 |
|
|
322 |
211 |
熱處理信息：
| 熱處理溫度區(qū)間 |
|---|
| Heat treated : 1993°C - 1316°C |
對照表（同等等級）信息：
| 型號 |
標準 |
國家 |
應(yīng)用 |
|---|
| Q255 A |
|
China |
Engineering and welding |
| ASTM 1030 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1005 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1006 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1008 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1010 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1013 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1015 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1016 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1017 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1018 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1019 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1020 |
ASTM |
USA |
General use carbon steel bar |
| ASTM 1021 |
ASTM |
USA |
General use carbon steel bar |
| 7Mn15Cr2A13V2WMo |
|
China |
Alloy tool steel - Without magnetic steel mold |
| SM2CrNi3MoAl1S |
|
China |
Plastic mould with flat steel |
| W6Mo5Cr4V2Al |
|
China |
High-speed tool steel |
| YG6A |
|
China |
Hard alloy tungsten cobalt class |
| YG8A |
|
China |
Hard alloy tungsten cobalt class |
| ASTM W1-A |
ASTM |
USA |
Carbon tool steel |